Category: Product

Al2O3 Content: 48% Shape:: Powder Bulk Density:: 2.1g/cm3 Cold Modules Of Rupture:: 7MPa Max Service Temperature:: 1300℃ Permanent Linear Change:: ±0.4 Alkali-Resistance:: Grade 1 Cold Crushing Strength:: 70MPa     Alkali resistant castable refractory material For Calciner , Powder Shape Read More

Al2O3 Content: 75% SiO2 Content: 20% Shape:: Powder Product Description 1. Profession manufacturer with 25 years experience 2. Steel Fiber Wear-Resistant Castable 3. High quality and low price Refractory Castable Introduction: Steel fiber high-strength wear-resistant castable is a kind of Read More

Al2O3 Content: 80% Bulk Density:: 3.0g/cm3 Shape:: Powder     Condrum Mullite Refractory Castable , Insulating Castable Refractory Cement   Product Feature:   High Strength Wear-Resistant Corundum Mullite Refractory Castable has high crushing strength, good high temperature volume stability and Read More

Al2O3,%: 72 MgO(%)≥: 11 Bulk Density (g/cm3)≥: 2.9-2.8 Modules Of Rupture (MPa) ≥: 9 Cold Crushing Strength (MPa) ≥: 60 Amount Of Water(%): 5.0-6.0 Linear Change(%)110℃.24h: 0-0.2 Linear Change(%)1550℃.3h: 0.5-1.5 SiO2(%)≥: 9.5 Aluminum And Magnesium Ladle Refractory Castable For Ceramic Read More

Al2O3,%: 75 Refractoriness ℃: 1770 Linear Dimensional Change %: -04 Cold Crushing Strength MPa ≥: 60-70 Breaking Strength MPa ≥: 11-12 Maximum Service Temperature ℃: 1400 High Alumina Self Flowing high temperature castable refractory RSGLJ -2 for Glass kiln Features Read More

Refractoriness (Degree):: Common (1580°< Refractoriness< 1770°) Bulk Density G/cm 3≥: 2.8 Cold Crushing Strength MPa 1110℃x3h≥: 100 MOR Mpa,≥: 12-14 Al2o3(%),≥: 85 Linear Dimensional Change%,≤: ±0.5 Gunning Dense Castables Features 1. Good adhesion. 2. High strength. 3. Low rebound rate. Read More

Al2O3%≥: 63 Fe2O3%≤: 1.2 SiO2%≤: 1.2 R2O%≤: 0.4 Fe2O3(%),≤: 0.8 Cl%≤: 0.1 325 Mesh Remind≤: 5 Surface(m2/kg)≥: 380 Initial Setting Time, Min≥: 120 Final Setting Time, Min≤: 420 High Alumina Cement Features 1. Early high strength, hardening quickly. 2. Resistance Read More

Refractoriness (Degree):: Common (1770°< Refractoriness< 2000°) Al2O3%>: 65 Bulk Density G/cm 3≥: 2.5 Cold Crushing Strength MPa 1110℃x3h≥: 80-90 MOR Mpa,≥: 10-12 Linear Dimensional Change%,≤: ±0.5 Insulating High Aluminum low cement castable refractory material for Steel furnaces 1. High strength.2. Anti-scouring.3. Read More

Bulk Density (g/cm3)≥: 0.5 Rervice Temperature (℃): 1150 Thermal Conductivity (W/m.k) ≤: 0.15-0.20 Cold Crushing Strength(MPa)≥: 1.5 Permanent Linear Change(1000℃.3h,%): -1.5 Heat resistant Refractory castable , Light weight Insulating Castable for furnace linings Features   1. Light weight, low bulk Read More